Product description
Generally, class 10.9 is used for mini-medium vehicles, class 12.9 is used for large-sized vehicles! The structure of the hub bolt is generally a knurled key file and a threaded file! And a hat head! Most of the T-shaped head wheel bolts are above 8.8 grade, which bears the large torsion connection between the car wheel and the axle! Most of the double-headed wheel bolts are above grade 4.8, which bear the lighter torsion connection between the outer wheel hub shell and the tire.
Designed for flat steel rims, they won't come loose on their own when properly assembled.
Jinqiang wheel nuts are rigorously tested and certified by independent agencies and certification bodies.
Our Hub bolt quality standard
10.9 hub bolt
hardness | 36-38HRC |
tensile strength | ≥ 1140MPa |
Ultimate Tensile Load | ≥ 346000N |
Chemical Composition | C:0.37-0.44 Si:0.17-0.37 Mn:0.50-0.80 Cr:0.80-1.10 |
12.9 hub bolt
hardness | 39-42HRC |
tensile strength | ≥ 1320MPa |
Ultimate Tensile Load | ≥406000N |
Chemical Composition | C:0.32-0.40 Si:0.17-0.37 Mn:0.40-0.70 Cr:0.15-0.25 |
Advantage
• Quick and easy installation and removal using hand tools
• Pre-lubrication
• High corrosion resistance
• Reliable locking
• Reusable (depending on usage environment)
Selection of high-strength bolt raw materials
The correct selection of fastener materials in fastener manufacturing is an important part, because the performance of fasteners is closely related to its material. Cold heading steel is a steel for fasteners with high interchangeability produced by cold heading forming process. Because it is formed by metal plastic processing at room temperature, the deformation amount of each part is large, and the deformation speed is also high. Therefore, the performance requirements of cold heading steel raw materials are very strict.
(1) If the carbon content is too high, the cold forming performance will be reduced, and if the carbon content is too low, it will not be able to meet the requirements of the mechanical properties of the parts.
(2) Manganese can improve the permeability of steel, but adding too much will strengthen the matrix structure and affect the cold forming performance.
(3) Silicon can strengthen ferrite to reduce cold forming properties and material elongation.
(4) Other impurity elements, their existence will cause segregation along the grain boundary, resulting in the embrittlement of the grain boundary, and the damage to the mechanical properties of the steel should be reduced as much as possible.
FAQ
Q1: What's the delivery time?
It takes 5-7 days if there is stock, but takes 30-45 days if there is no stock.
Q2: What's the MOQ?
3500pcs each products.
Q3: Where is your company?
Located in Rongqiao Development Zone, Nan'an City, Quanzhou City, Fujian Province, China.
Q4: Can you offer price list?
We can offer all parts which we handing brands, as the price is fluctuating frequently, please send us detailed inquiry with parts number, photo and estimated unit order quantity, we will offer the best price for you.
Q5: What else products you can make without wheel bolt?
Almost all kinds of truck parts we can make for you. Brake pads, center bolt, U bolt, steel plate pin, Truck Parts Repair Kits, casting, bearing and so on.